Résine UV PrimaCreator Value Flex - 1L

There PrimaCreator Value Flex UV Resin 1000ml - Black It's the ideal resin for those seeking extraordinary flexibility, strength, and precision in 3D printing. Thanks to a formula optimized for LCD, DLP, and SLA printers with 395–405nm UV light sources, it allows you to print elastic, impact-resistant, and highly detailed objects. It's perfect for models that require resilience, the ability to bend without breaking, or shock absorption, such as gaskets, flexible mechanical components, handles, covers, and functional prototypes.

The surface of the models is matte, smooth, and features sharp details: the special mix of Value Flex allows the printed object to achieve exceptional elongation at break (up to 130%), optimal hardness, and impact resistance superior to standard resins. The overall printing experience is simple and rapid thanks to short curing times: the resin hardens in seconds under UV light and can be quickly post-cured.

Technical specifications

• Technology: UV/DLP/LCD, light source 395–405nm
• Color: black (also available in other colors)
• Hardness (Shore D): 65–75D
• Elongation at break: up to 130%
• Impact resistance (notched): 41–48J/m
• Tensile strength: 30–52MPa
• Tensile modulus of elasticity: 1,779–2,385MPa
• Bending strength: 40–70MPa
• Flexural modulus: 1,882–2,385MPa
• Viscosity: 150–300mPa s (25°C)
• Density: 1.05–1.25g/cm³
• Glass transition temperature: 100°C
• Thermal Deformation Temperature (HDT): 80°C
• Volumetric withdrawal: 3.72–4.24%
• Linear withdrawal: 1.05–1.35%
• Thermal expansion: 95×10^-6
• Curing time: 4–12s for 0.05mm layer; background 40–60s
• Post-curing: 2–5min UV camera, 10–20min in the sun
• Surface: matte finish, high detail, soft touch
• Compatibility: Wanhao Duplicator, Anycubic Photon, Zortrax Inkspire, and most desktop UV printers
• Odor: very low; also suitable for use in domestic environments
• Quick post-print cleaning (requires IPA)
• Directions for use
• Shake well before use.
• Clean models with IPA (isopropanol) after printing.
• For functional objects and elastic prototypes, adjust parameters to achieve maximum flexibility.
• Post-cure as directed to achieve maximum mechanical performance.